CZ型彩磚光亮劑sulfonated melamine series resins

一、用途及特點
本品在反打振動密實成型混凝土彩色人行道地磚工藝中使用，能明顯提高地磚早期強度和后期強度、提高表面光潔度和裝飾性，同時還具有抑制制品返霜和延緩制品的褪色功能。該劑具有使彩色面層持久保色、色彩鮮艷、光滑亮澤等特點，并且顯著提高耐磨性及抗壓強度和抗折強度，顯著提高抗?jié)B性，增強抗凍融能力，提高耐久性。
二、執(zhí)行標準：GB8076－1997
三、主要技術指標

The brightening agent used for the colour road face brick is an addition agent which is mainly made of sulfonated melamine-formaldehyde resin．
This brightening agent has the functions of increasing and strengthening the colour and let the road brick has bright-colour surface．Also，it can prolongs the colour fade time.This product is a yellowishtransparent liquid or a white powder．It is non-poisonous，non-sitmutant，and non-corrosive material and does not pollute the environment．It can strongly adapt various colour cements and pigments．This product is mainly used to produce the colour road face brick products，the colour cement tiles or other high bright surface colour concrete products which are made of the colour cement，the white cement and the common silicate cement．
Main Index
Outward Appearance: Non-colour or yellowish transparent liquid
PH Value：9＋/-2
Solid Content(％)：38＋/-2
Spread Rate(mm)：>200
Viscosity(CP)：20～40
Performance And Functions
1．It not only can be used to produce the artificial marble and terazzo，but also can obviously improve the colour of the decoration concrete products made by the common technology．It can make the concrete product surface bright and clean like the procelain．
2．The cement brightening agent can adapt with Portland Cement or various colour cements very well.They all can get the same effects of brightening and keeping the colour well．It also can prevent the concrete surface to be suffused with white.
3．The cement brightening agent has a certain of water reduce effect for the cement mortar pr concrete，and makes the cement mortar or concrete has more early strength。Thus，it can speed up the turnover of the models and enhance the product quality．
4．The cement brightening agent has not the air-initiation effect．It only contain very small amount of the chloric ion(about 0.03～0.04%CL-)，so it has not the rust and corrosion effect to the iron bars．
5．The cement brightening agent can be used together with the other addition agents and does not influence the brightening effect of the cement product surface．
Application Method
1．The addition amount of the brightening agent is 3～5％ of the cement(generally 4％)．The higher of the addition amount,the better of the effect，the higher of the product strength，the brighter of the product surface，the stronger of its anti-abrasion．
2. First,the brightening agent is dissolved into 70～80％of the water which is used for mixing the cement．Then，slowly add it into the mixture of the cement and aggregate and mix them fully．If the thickness of the mortar is dryer，add into some water and fully mix them again to adjust the thickness．
3．Add the mortar into the model and vibrate it for about 10 seconds．More Vibration time will influence the brightness of the product surface．

增色、固色、賦予路面磚光亮鮮艷的面層
Increase and strength the colour and let the brick has bright-colour surface

彩色路面磚光亮劑是采用磺化三聚氰胺甲醛樹脂為主要原料制造而成的一種
外加劑。這種光亮刑具有增色、固色等功能，能賦予路面磚光亮鮮艷面層，
相對延長褪色時間。該產(chǎn)品為無色至微黃色透明液體或白色粉劑，無毒、無刺激性、
無腐蝕性，不對環(huán)境產(chǎn)生污染。與各種水泥、顏料均具有很強的適應性。產(chǎn)品主要
用于彩色水泥、白水泥、普通硅酸姑水泥生產(chǎn)彩色路面磚制品，以及彩色水泥瓦或其
他需要增強和提高表面光潔皮的彩色混凝土制品。

1 、主要指標
外觀：無色或微黃色透明液體，白色粉末
PH 值： 9 ± 1
含固量 ( ％ ) ： 38 ± 2
擴散力 (mm) ： >200
粘 度 (CP) ： 20~40

2 、產(chǎn)品性能與應用
1 、它不僅可用于人造大理石和水磨石，而且可明顯改善用普通混凝土路面磚的彩色效果，使混凝土具有光亮的表面。
2 、光亮劑對水泥適應性較好，無論是普通水泥或彩色水泥都能起到同樣的增光保色效果，同時可預防混凝土表面泛白。
3 、光亮劑對水泥砂漿有一定的減水作用，使水泥砂漿早強和增強， 由此可見加速模具的周轉，提高制品的正品率。
4 、光亮劑無引氣作用，對鋼筋無銹蝕。
5 、光亮劑可與其他外加劑一起使用，不影響光亮效果。

3 、使用方法：
1 、光亮劑摻量約為水泥面料用量的 3~5 ％ ( 常用量為 4 ％ ) 。摻量越多，效果越好，制品強度更高，更光亮更耐磨。
2 、先將光亮劑溶于 70~80 ％的面料拌合水中，再慢慢加入正在攪拌的面料內(nèi)，充分攪拌，觀察面料稠度，可加多余的拌合水調(diào)節(jié)至適宜稠度。
3 、加入光亮劑的彩色面料入模后振動時間控制在一定時間內(nèi)，不宜過長，否則會影響光亮度。

彩色路面磚光亮劑

一、概述
　　 彩色路面磚光亮劑是采用磺化三聚氰胺甲醛樹脂為原料配制而成的一種外加劑。這種光亮劑具有增色、固色等功能，能賦予路面磚光亮鮮艷面層和相對延長褪色時間。
　　 使用光亮劑后：混凝土早期強度提高，脫模周期縮短，模具周轉加快。降低模具投資。制品正品率提高，脫模后制品表面光潔、無色差色斑，彩色更加艷麗奪目。路沿石自潔能力提高，表面塵土在雨水；中洗下能自潔如新。與各種水泥、顏料的適應性強，可與其他外加劑一起使用，適用范圍廣。
　　 本產(chǎn)品與各種水泥具有很強的適應性．產(chǎn)品主要用于彩色水泥、，白水泥、普通硅酸鹽水泥生產(chǎn)彩色路面磚制品，以及彩色水泥瓦或其他需要提高表面光潔度的彩色混凝土制品。

二、技術數(shù)據(jù)
外觀：粉劑為白色粉末。液體為無色透明液體
含水率 (%) ( 粉劑 ) ：小于 3 。
固體含量 (%) ( 液體 ) ： 38 ± 2
PH 值 ( 20 ℃ ) ， 20% 容液： 9 ± 1 。
硫酸根離子含量 (%) ： 2.6
氯離子含量 (%) ： 0.03~0.04

三、規(guī)格
本產(chǎn)品分為：
粉末， 40% 溶液。

四、功能
1 、不僅可用于人造大理石和水磨石，還可改善普通工藝制成的裝飾混凝土的色彩效果；
2 、對水泥適應性好，無冷普通灰水泥或彩色水泥都能起到同樣的增光保色效果；
3 、對水泥砂漿有一定的減水作用，使水泥砂漿早強和增強，由此可加速模具的周轉，并提高正品率；
4 、可與其他外加劑一起使用，不影響其光亮效果。

五、包裝
粉末：塑料密封袋裝，每袋 20 公斤 。液體：桶裝，每桶 250 公斤 。

六、儲存
粉末易吸潮，應在密封的原裝袋中存放，并置于干燥的地方。儲存期：一年。液體儲存期： 6 個月。

七、運輸規(guī)定
不燃，無毒，一般運輸要求。

　　為您的橋梁、隧道、水泥制品等清水混凝土工程，幫你達到內(nèi)實外光的新突破。
　　本產(chǎn)品能大大改善混凝土外觀，可達到光亮、保潔的技術效果，使混凝土在惡劣的環(huán)境下，因提高外觀的光、潤、亮，使其混凝土在抗侵蝕、沖刷、耐磨、防腐蝕、內(nèi)實外光等方面取得了重大的技術突破。
　　同時：具備了高減水，無氯低堿，高抗?jié)B、超塑化、緩凝、早強、保水性及可泵性優(yōu)良等特點。
本產(chǎn)品彌補了外加劑單體系列在各工種混凝土應用中的早期缺陷，對混凝土外觀要求較高的工程提供了亮潔的技術保證，取得了外加劑應用技術的超疊加效應。

Brightened agent of colored road brick

一、 Description
　　 The brightened agent of the colored road brick is an addition agent made of 磺化三聚氰胺甲醛樹脂 .This brightened agent has the functions of the color promotion and the color strengthening . It can entrust the bright –colored surface layer to the road brick . And prolong the time of the color keeping .

　　When this product is used : the early strength of the concrete is increased, the curing time before the model taking off is shortened. The model turnover period is quicker ,and the cost of the model is reduced, the percentage of the quality product is risen. The surface of the brick will be bright and clean without the color difference and the color spots ,the self-clean ability of the road side stone is enhanced , the dust on the surface of the bricks can be taken off by the rain . This product can be suitable for various cements and the gypsum .It also can be used together with the other additives . Its suitable application range is very wide .

　　This product has very strong adaptability with the various cement . It is mainly used in colored cement , white cement , and common silicate cement to produce the colored road face brick products and the colored cement tiles or other colored concrete products which are needed to improve their surface to be bright and clean.

二、 Properteis
Outward appearance: White powder or colorless transparent liquid.
Water content(powder) (%): ＜ 3
Solid substance content (liquid) (%):38+/-2
PH value (20degree C. , 20% so lution ):9+/-1
SO 4 ion content (%):2.6
Cl ion content (%):0.03 0.04

三、 Specification
Powder, 40% solution

四、 Suitable application range
1 、 It can be used not only for manufacturing the artificial marbles and the terrazzo , but also to improve the color effect of the decoration concrete produced by the common technology.
2 、 It can make the cement products have the bright surfaces and the color-keeping ability , whether they are made by the common cement or the colored cement.
3 、 It has some water reducing effect for the cement mortar and can enhance the strength of the mortar. It can quicken the model turnover and enhance the percentage of the quality products.
4 、 It can be used together with the other additives and does not influence the bright effect.

五、 Package
Powder: plastic sealed bag . 20kg per bag . Solution: in bulk 250kg drum .

六、 Storage
This powder is easy to absorb the moisture from the air . So it must be kept in the original sealed bag and stored at the dry place .The storage period is one year .

七、 Transportation
This product is non-toxin and non-flammable . So the transportation requirement is general.

[ 應用實例 1]

光澤型彩色混凝土路面磚的生產(chǎn)與應用

一、光澤彩磚特性
　　 采用壓制成型工藝生產(chǎn)混凝土路面磚，經(jīng)過幾年使用，耐污性、耐磨性差，色彩不鮮明，褪色快等，致使裝飾效果逐漸減退或磨蝕損壞。
(1) 裝飾性能好 根據(jù)檢測，磚面光澤度一般在 20 光澤單位以上，最高達到 50 光澤單位，接近一般室內(nèi)地面裝修材料，因而使得磚面光滑亮澤，色彩鮮艷，具有良好的裝飾效果。同時，由于樹脂的應用，使得飾面層結構致密，毛細通道大大減少，因而，產(chǎn)生鹽析的可能性也大大降低，從而解決了長期存在于路面磚磚面因鹽析而產(chǎn)生白斑的問題，這對于保持磚面的裝飾效果具有重要作用。
(2) 顏色耐久性提高 由于飾面層表面光滑，結構致密，可以反射較多陽光，減少了干溫循環(huán)、空氣中有害氣體以及酸性介質(zhì)等的影響，因此，磚面顏色褪色速度有了一定程度降低。根據(jù)我們在自然條件下的測試，與壓制彩磚相比，光澤彩磚磚面顏色的褪色時間一般延長了一年以上。
(3) 耐磨性好 由于飾面層中采用了花崗巖耐磨細骨料，這種細骨料除了作為砼的一種組成材料之外，還能顯著提高飾面層耐磨性。此外由于飾面層結構密實，砼強度高，這也對飾面層耐磨性起著決定性作用。檢測結果表明，光澤彩磚磚面耐磨性能大大高于標準 (JC44 6 － 92) 優(yōu)等品要求，這對保持磚面的裝飾效果，延長產(chǎn)品使用壽命，有著重要影響。
(4) 產(chǎn)品尺寸準確 光澤彩磚采用塑料模具成型，在生產(chǎn)過程中，因塑料模具不象壓制成型所用鐵模，存在較大磨損，因此所生產(chǎn)的產(chǎn)品規(guī)格尺寸十分穩(wěn)定，一般尺寸偏差小于 0.5mm 。
(5) 早強高強 產(chǎn)品實際抗壓強度不小于 40MPa ，抗折強度不小于 5.0MPa ，均高于標準優(yōu)等品要求 30 ％以上。
　　 有關質(zhì)檢部門根據(jù) JC44 6 － 91 行業(yè)標準對本公司生產(chǎn)的光澤彩磚進行了全面檢測，結果表明其各項指標均達到優(yōu)等品要求 ( 詳見表 1) 。

二、光澤彩磚的生產(chǎn)
1 、原材料技術要求
(1) 水泥 飾面層一般選用 425 ＃ 以上白色硅酸鹽水泥或彩色硅酸鹽水泥；結構層可選用不低于 42 5 ＃ 硅酸鹽水泥及普通硅酸鹽水泥。
(2) 骨料 飾面層采用粒徑 2 ～ 5 ㎜花崗巖石米；結構層采用 5 ～ 15 ㎜ 碎石 ( 卵石 ) 及中粗砂。
(3) 外加劑 慕湖牌光亮劑固含量 36 ～ 40 ％， PH 值 8 ～ 10 ，密 度≥ 1.2g /ml ，不得有沉淀或發(fā)黑發(fā)臭現(xiàn)象。
(4) 顏料 用于飾面層砼的顏料應滿足如下要求：①耐堿性應為 1 級；②耐光性達到 7 級以上；③著色力強，即在摻 量≤ 10 ％時，色彩濃度滿足使用要求；④分散性好；⑤耐光性、耐大氣腐蝕性好；⑥不應有明顯的破壞水泥凝結、硬化作用。

2 、主要生產(chǎn)設備、設施要求
(1) 砂漿攪拌機，用于飾面層砂漿的攪拌。
(2) 強制式攪拌機或自落式攪拌機，用于結構層砼攪拌。
(3) 振動臺，用于光澤彩磚底、面層砼結構成型。振動頻率為 2800 ～ 3000 次 / 分，振幅為 0 ． 3 土 0 ． 05mm 。
(4) 塑模 應滿足如下要求：①具有一定剛性，變形小；②耐磨性能好：③具有較好韌性，抗沖擊能力強；④耐熱，使用溫度為 -40 ～ 80 ℃ 時，性能不發(fā)生明顯變化；③化學穩(wěn)定性好，能耐水、鹽和堿；⑥具有較好的耐候性；⑦模內(nèi)表面光澤度≥ 50 光澤單位。

3 、飾面層砼配合比設計原則
　　 飾面層砼配合比是決定光澤彩磚性能與質(zhì)量的一個重要因素。要配制好飾面層砼，應科學合理地處理好以下三方面關系：

表 1 光澤彩磚技術性能指標檢測情況

(1) 集灰比 即花崗巖細骨料與水泥用量之比。由于花崗巖的硬度大大高于水泥石的硬度，因此適當提高花崗巖細骨科在飾面層砼中的比例，有利于提高磚面的耐磨性。同時，由于花崗巖細骨料價格較彩色水泥便宜得多，故適當提高集灰比，還能顯著降低產(chǎn)品的材料成本。但若集灰比過大，則砼結構難以成型密實；集灰比過小，會造成飾面層收縮過大，產(chǎn)生分層和龜裂現(xiàn)象。根據(jù)花崗巖細骨料顆粒大小及級配情況，集灰比一般控制在 1.5 ～ 2.0 之間為宜。
(2) 聚灰比 即光亮劑用量與水泥用量之比。適當提高水溶性樹脂及助劑摻量，可顯著改善飾面層砼的粘結性、耐久性和耐磨性，減少收縮，提高不透水性、耐腐蝕性和耐沖擊性，同時還能提高磚面光澤度。但若摻量超過一定限度，上述性能不再明顯改善，相反，會對生產(chǎn)和產(chǎn)品性能造成不利影響，如磚面脆性增加，易粘模以及成型凝結時間過長等問題。此外，由于光亮劑價格較高，多摻也不經(jīng)濟。一般根據(jù)水泥品種不同，聚灰比控制在 0.015 ～ 0.07 之間。
(3) 水灰比 由于光亮劑含有大量 OH — 族，對各種材料特別是水泥顆粒有較強的吸附作用，可顯著改善新拌砼和易性，大大降低水灰比，因此，在滿足飾面層成型要求的前提下，應盡可能發(fā)揮水溶性樹脂的這種減水作用，降低水灰比，以提高飾面層砼各齡期尤其是早期強度，改善磚面耐磨性等各項性能。

4 、生產(chǎn)工藝
4.1 生產(chǎn)工藝流程 ( 見圖 1)

4.2 生產(chǎn)工藝控制要點
(1) 原材料的質(zhì)量控制
　　 原材料質(zhì)量控制的重點是搞好光亮劑的質(zhì)量控制，光亮劑是影響光澤彩磚飾面光澤度的關鍵因素，也是影響光澤彩磚其它各項性能的主要因素之一，此外光亮劑質(zhì)量若不好，還會造成粘模、磚面白斑等產(chǎn)品質(zhì)量問題。因此，搞好光亮劑質(zhì)量控制是搞好光澤彩磚生產(chǎn)的關鍵所在。光亮劑質(zhì)量控制可從以下幾方面著手：①按標準檢驗，做到合格入庫；②采用塑料容器密封貯存；③保證適宜貯存環(huán)境；④按期使用。

(2) 面層料漿攪拌的控制
面層料漿攪拌主要控制好投料順序與攪拌時間。具體如下：

(3) 飾面層成型的控制
　　 飾面層成型主要控制好以下三點：一是盡量排除內(nèi)部氣泡，使結構成型密實；二是保證料漿均勻鋪展，避免厚薄不均；三是在滿足前兩個成型要求的前提下，盡量縮短成型時間。

(4) 飾面層靜停凝結時間的控制
　　 飾面層成型好后，需要靜停凝結一段時間，使飾面層料漿形成初步的凝聚結構，這樣在結構層成型時，加入的砼混合料就不會透過飾面層，影響磚面美觀。但靜停時間不宜過長，否則會影響飾面層與結構層之間的粘結，造成分層破壞。一般飾面層靜停時間以不超過 45 分鐘為宜。

　　因此，脫模時間就選擇在成型后的第三天或第四天比較合適。

(6) 貯存與養(yǎng)護的控制
　　 脫模后，由于光澤彩磚內(nèi)部含有較多水份，光亮劑與細骨料及水泥水化產(chǎn)物之間還未完全牢固結合，易于受到活性介質(zhì) ( 如水等 ) 的侵蝕，使磚面喪失光澤。因此，在脫模后一段時間內(nèi)光澤彩磚不宜浸水或在濕度過大的環(huán)境下貯存與養(yǎng)護。但若貯存環(huán)境過于干燥，光澤彩磚內(nèi)部水分過度蒸發(fā)，水泥水化就會終止，不利于光澤彩磚結構砼強度發(fā)展，影響產(chǎn)品質(zhì)量。表 2 是光澤彩磚在不同濕度條件下養(yǎng)護 14 天后所測得的結果。
　　 從表 2 可以看出，若兼顧光澤度與抗壓強度兩項質(zhì)量指標，光澤彩磚在初期的貯存保養(yǎng)中，保證 70 ％～ 80 ％的濕度環(huán)境是必要的。

表 2 濕度對光澤彩磚光澤度與強度的影響

三、光澤彩磚的應用

3.1 應用效果
　　 實際使用表明，光澤彩磚的耐污性、耐磨及耐久性等性能均明顯優(yōu)于壓制彩磚，尤其是光澤彩磚的裝飾美化作用更在壓制彩磚的基礎上大大提高了一步，改變了壓制彩磚粗糙灰暗的形象。

3.2 防滑措施
　　 由于光澤彩磚表面光滑，為防止行人滑倒，應采取防滑措施。主要措施有：①磚面設置深度為 2 ～ 5mm 線糟，使磚面本身具有防滑功能；②在坡度較大的路面采用階梯式鋪筑；③搞好路邊排水，避免路面積水。